Depending on the grade of PEEK you have, you will be able to print with this machine. It's just case of whether you can control crystallinity during the process.For a "low" temp system which is what...
Type: Posts; User: CSMonkey
Depending on the grade of PEEK you have, you will be able to print with this machine. It's just case of whether you can control crystallinity during the process.For a "low" temp system which is what...
No you wouldn't, the cost would be uneconomical and the amount of post finishing to make a usable injection mould tool would negate any benefit.
Plus you then need an injection moulder that can...
Stratasys Soluble Support material is not PLA, and to remove you use a heated water tank with diluted sodium hydroxide. Wear gloves and goggles when handling the solutions and be prepared to...
You are missing something....
Insulators are not ESD as they can't be grounded and static charge will remain.
https://en.wikipedia.org/wiki/Electrostatic_discharge_materials
The old Zcorp software [now 3DSystems] allowed you to wrap a colour image around a part and print in full colour [in gypsum]
Several software packages have the feature to create a 3D relief from a...
Please don't fill this forum with multiple threads about your issues with a company and their forums.
One thread explaining the problem is all that's required.
Thanks
Stratasys [Objet] make a range of flexible photopolymers for their printhead range of machines. For true silicon you would need to look at Picsima who developed a way to print RTV silicones
Rich
Just be aware that the Dimension 768 is now classed as end of life by Stratasys, so limited spares and parts should the machine need any maintenance. The SST uses P430 material cans whilst the 768...
You mean something like this
http://www.keep-art.co.uk/Self_build.html
A ceramic paste extruder
Try https://grabcad.com
So if I've got this correct, you've got a 50x50x0.8mm geometry made up of lots of sections of 0.2-0.7mm.
I don't know which technology you are planning to use, but you are going to struggle with...
Try contacting JH May models and prototypes. They already offer a rapid casting service from SL resin models, so they are probably the best placed to speak to about this process.
...
Locate the free version of Netfab Basic, which is STL manipulation and build processing software.
Using the edit function you can manually delete triangles which make up the detail of your hole...
What's your point? Are metal AM parts better than traditional?
Answer - NO they are different with different pros and cons.
If you could find the resin used by Invisalign, then you would have a product that has been certified for oral applications. They SLA customised dental retainers for correcting your teeth, and have...
There are a number of academic papers on research into why LS powder is degraded during the process, and why you need to blend used with new to re-use in the sintering process.
In it's simplest...
That is how I connected my thermocouple board. Did you edit the correct section of pins.h? as in scroll down to the correct board number definitions. My RAmbo board is 301 in the sketch.
Rich
I used the Analog input pins [left of the main chip in your image]
You have to change the Marlin sketch, specifically Pins H to tell the board which pins to look at for temperature....
Wendy, your K200 advert that you linked claims the machine has an E3D hotend, when the photo clearly shows a rough casting which is copied from their machined product.
As someone who works with...
EOS have a metal laser melting system that works with 18 carat gold directly.
https://www.eos.info/precious-m-080
In Netfab, right click on the part name in the right hand editor tree and go through the menu to the repair section.
In your modeller window the repair options appear above the model on the...
Complicated if you don't have any experience with OpenScad. Magics or the free version of Netfab makes this a much simpler job. Visual editing of the STL is a lot simpler for people not used to CAD....
Or download Netfab Basic [free] and edit the stl file. Delete the sidewall triangles and use the hole repair tool to add triangles across the remaining gaps.
Rich
Projet 660 if I remember is the new name for the ZCorp plaster machine.
Any distortion has nothing to do with heat, that's not how this process works. It's the mass of the binder infused geometry...
Our local library [Exeter] has a Fab Lab inside with a number of technologies available.
https://www.fablabdevon.org/