Quote Originally Posted by jfkansas View Post
No never jammed one, but imagine i could be drilled out if you had to. Just not sure if you could ever get all the char out of the nozzle. It is soft stuff too so best to use a PTFE lined hot end.
Which means to me that it is more likely to jam up in the extruder drive mechanism. Have you heard anything yet regarding the new Flexion hi-temperature product? I have not, nor do I see any mention of it on their website.