Quote Originally Posted by DarkAlchemist View Post
Looks and adding more surface area so it can cool down a tad more/quicker?

Seems really backwards to print clips in a material that has a Tg below, or at, the print bed's temp that you normally print at. Now if someone used Bakelite for these then I would be saying rock on but printed clips do get soft if ABS and PLA you might as well not even try.
They are not the best solution but many people have had good success with them so I believe your statement of "you might as well not even try them" is in error.