Results 1 to 10 of 13
Thread: What plastic for Printer Parts
-
10-26-2015, 03:40 PM #1
- Join Date
- Jul 2014
- Posts
- 305
What plastic for Printer Parts
I want to change out a lot of parts in my printer for 3D printed parts. Right now I only have PLA but I want to buy something better suited for the part.
I have been reading and I think PETG is a good choice. Is this a good choice or what would you choose? These parts would be near the hotend for cooling and gears for the belts so they will experience heat and stress.
-
10-26-2015, 07:10 PM #2
PETG is a good choice...
-
10-27-2015, 05:13 AM #3
-
10-27-2015, 05:57 PM #4
- Join Date
- Jul 2014
- Posts
- 305
The design in many aspects is basic from Makerfarm. I am looking to increase the details of my prints which means changing the X axis where the belts are mounted and changing a few more things.
-
10-28-2015, 01:12 AM #5
Then I would make an alternative suggestion: Have your new parts machined from aluminium. You will benefit from the rigidity of metal parts over printed plastic parts.
-
10-28-2015, 09:12 AM #6
- Join Date
- Feb 2015
- Posts
- 371
I am curious what changes you would make. I see there may be room for improvement on the z as well. For example, the v slot wheels on my z don't all spin when the z is moving up and down. I can freely spin the inside wheels. Also, I'd like to firm up the z towers a bit. I see some resonance waves in the side walls which I think is from the towers rocking.
Building the the parts first from ABS or PETG is a good way to prototype. I have used ABS with good results.
-
10-28-2015, 08:19 PM #7
This indicates to me that you did not have the left x-motor and right hand x-idler brackets properly adjusted to the vertical rails and the two brackets level with each other BEFORE you tightened up the horizontal rails to the end brackets.
EDIT: ...regardless of whether or not the build guide was clear on doing this. It certainly wasn't mentioned in the April 2014 build guide that I used.
EDIT #2: With the horizontal rails loose on the x-motor and x-idler brackets, adjust each of the x-axis brackets to their respective vertical rails. Then level the two x-brackets using the method of your choice. I used a long metal ruler as a straightedge across the top of the two brackets. Others have adjusted for something like equal distance between the bottom of the brackets and the tops of the z-motor mounts. Then, and only then, tighten the horizontal rails to the x-motor and x-idler brackets. Tightening the eight M5 bolts on the horizontal rails will likely torque the x-axis assembly out of alignment, so some readjustment or pre-tensioning in the opposite direction may be necessary.Last edited by printbus; 10-29-2015 at 03:01 AM.
-
10-29-2015, 08:03 AM #8
- Join Date
- Feb 2015
- Posts
- 371
Thanks printbus, yes it is finicky. There wasn't anything in the guide about this. I did do it as you mentioned on my initial build, without the leveling step. I noticed the freely spinning wheel and redid it buy loosening the x brackets and then adjusting the cam wheels, then leveling and tightening it up. I need to do it again I guess and take a bit more time. I really like how the MTW Mendalmax 3 is put together. Their x-axis and extruder mount system is very robust and makes adding dual extruders effortless. I see many correlations to the new pegasus printer and the MM3.
I would look for inspiration there if making changes. I have seen some pretty amazing prints from those. It has taken me many hours of tinkering and tweaking to even come close to the results a colleague is getting from his MM3.
-
10-29-2015, 08:40 PM #9
- Join Date
- Jul 2014
- Posts
- 305
I received my roll of Hatchback 1.75mm PETG in white, but I am printing a series of parts that I am selling. So I will finish that first before fiddling with PETG.
-
11-08-2015, 08:55 AM #10
- Join Date
- Jun 2014
- Posts
- 349
Aluminum is an interesting option. Maybe someone will start selling them. I guess it would need to be a hollow frame to keep the weight down.
Mine are currently PLA, but I want to make them PETG. However in either case, if the extruder fan breaks, the heat might go up and melt something. At least PETG will last a bit longer, but aluminum would be great here.