you migh want to look at pet-g, rather than abs,

If it's for 'click together' joints then pet-g is way way better than abs. For everything else pla is going to be better than abs.

Pet-g has a lot more 'give' than abs. It's not as rigid or strong as pla - but it's 'tpugh' so is unlikely to crack if a particular joint is a tight fit.
And it's pretty easy to print with.