Now I am really frustrated. Two more aborted prints today. This time I loaded the print chamber with four of the test pieces, in a similar pattern to that shown in Roman's photo below. All four curled up at the edges and were dragged into the overflow bin with some of the molten Nylon sticking to the blade. This happened using the default values of; surface at 170C and chamber at 140C. For the second print I upped the surface to 175C and the chamber to 150C. This time was slightly better in that only three were wiped out - not much consolation!
However, there may have been a slight clue in the second print as the 'cake' surrounding the prints was much more solid than in previous attempts. In the first few prints there was very little 'cake' and the prints were surrounded by loose powder. In the last attempt, at 175C surface and 150C chamber, nearly all the powder in the print chamber was loosely holding together. So, just how solid should the 'cake' be and does this point to my surface temperature still being too low?
This is an extract that accompanied the photo from Roman's response to my ticket:
Also check the following things:
-the Laser glass may not cover the IR sensor
- the tube of the IR sensor may not touch the sheet metal beyond it
- The frontal light shade has to be adjusted correctly. the shade of has to be aligned exactly to the backside.
The last point is the one that is confusing me. I don't see much of a shadow on my powder or in the photo. If the frontal shade needs adjusting does it mean a complete disassembly of the hood? Not looking forward to that!!
Print surface.jpgLast edited by Mike Francies; 11-17-2016 at 11:05 AM. Reason: Cannot upload photo
-
11-18-2016, 01:55 AM #2
the chamber temperature does matter. But everthing between 140-150 C is fine. But the surface temperature is much more important, a difference between 1-2 C can make the difference between a failed and a sucssesful print!.
As I already stated your temperature distribution has to be alright before you can get start fine tuning your prints. Here is what you should do:
-Do not use custom settings for starting. For starting use the standart PA12 settings. You can experiment that later. The custom settings are meant for people that exactly know what they are doing.
-As rudschul stated the front sheet of the lamp has to be perfectly aligned with the backside of the powder surface. If its to far, the back will get to hot and the front to cold. If you have h shadown on your print surface your front will get to hot and back to cold. To get an even distribution it has to be aligned perfectly.
- Preheat your printer. about 1.5 hours should be sufficent
- load a calibration print (only one in the middle) and force the printer into powder prep mode
- raise your powder temperature 1 C.
- wait for about 1 min and check the powder.
- raise temperature again
- repeat until you see your powder darken/ get burned
- reduce temp 1.5 C ------> This will be your printing temperature
- if you hit 180 C and the powder does still not get burned check your sensor position / laser glass. Something might not be right.
I strongly discourage from preheat temperatures over 150 C as this will degrade your powder in short and long term! Also you run the risk of overheating! The problem here is when you heat your powder with temps over 150 for a long time it might graded and turn black witch results melting your powder in the build chamber. This will cause serious damage to your printer.
A little fluctuation is normal.