If you work austenitic stainless when cold it becomes magnetic. You have to heat it to make it austenitic again. This is why things like stainless steel kitchen sinks are magnetic, they have been cold worked. If you take it up to about 1200? degrees it becomes non magnetic again but the wife whinges 'cos the sink aint shiny any more.