    How stiff are the parts made of your resin ?

    Hi guys,

    was wondering, how hard/stiff are the parts made out of your resin ? say, compare to PLA or ABS, or other materials ..

    One weakness of FDM, is the bonding force between layers, my parts will often fail due to this. Are the bonds stronger with your resin ?

  2. #2
    Kudo3D Representative
    Join Date
    May 2014
    Location
    San Francisco
    Posts
    31
    The resins we are using are not stiff enough for your applications. We will be certifying ABS-like material soon and will definitely keep you posted.
    Could you provide more details about the bonding force? Thanks!

  3. #3
    Engineer-in-Training Hugues's Avatar
    Join Date
    May 2014
    Location
    Switzerland
    Posts
    210
    ABS like stiffness would be great, and anything above that of course.

    By bonding force I was referring to the layers separation that we sometimes have with FDM.

    Are your parts more likely to fail at the layer interface ?

  4. #4
    Kudo3D Representative
    Join Date
    May 2014
    Location
    San Francisco, CA
    Posts
    29
    Hugues,

    We will offer ABS like material in the near future. Layer interface failure is rarely seen with SLA.
    It only happens when the resin is underexposure or when the lifting speed is too high. These can be
    prevented with proper printing parameters.

    Thanks!