Well there are a couple ways. Take a look at your perimeter layers as they go down. The edges should touch one another. If they dont them you need to up the multiplier so more plastic is extruded....
Type: Posts; User: jimc
Well there are a couple ways. Take a look at your perimeter layers as they go down. The edges should touch one another. If they dont them you need to up the multiplier so more plastic is extruded....
Yes thats extrusion multiplier. Sin e then i have upped it to around 94. Keep in mind that was for abs. Pla will be totally different.
you dont need to do that calibration. that is all set up in the firmware already. if you built a reprap printer then yes you would need to do it. the m2 is a ready to go system even if you buy it in...
No there is really no calibration for that unless you diving into the firmware setting.
What type of plastic are you printing?
layer bonding is too low a temp. as for what you are seeing there, you need to fine tune your retraction, coasting and restart distance. im not sure what slic3r calls these. coasting stop extrusion...