    Successful 1st ABS Print

    Just printed my first ABS model using a pre-sliced PLA models g-code, I did not even re-slice for ABS preheated 230C Nozzle 96C Bed selected the PLA FOB Fish g-code for Print and quickly Updated the Models PLA temperatures to the Preheated ABS values using the LCD.
    And this is the Result

    FOB ABS.jpg

    Actually it printed better than when using PLA, as I increased the fan speed to compensate for the higher ABS filament temperature.
    Allowing it to bridge better, may need to reevaluate the Fan setting I have for PLA in cura?

  2. #2
    Super Moderator curious aardvark's Avatar
    Join Date
    Jul 2014
    Posts
    8,818
    actually with things that contain internal joints, abs is generally better. Simply because it shrinks so much that the fine gaps netween sections come out better.
    That said it still stinks and the layer bonding is crap :-)
    As far as fan speed goes - pretty much 100% all the time will work best.

    The faster you can cool the extruded plastic, the better the print will be.

  3. #3
    looks good what printer are you using?

  4. #4
    Staff Engineer Roberts_Clif's Avatar
    Join Date
    Jun 2017
    Location
    Washington State, USA
    Posts
    1,141
    Add Roberts_Clif on Thingiverse
    Quote Originally Posted by aventr View Post
    looks good what printer are you using?
    It is a Hictop 3DP12 Aluminum frame printer

    I bought both My 3DP11 and 3DP12 for around $200 they were One Owner Barely Used units that for one reason or another could not be made to operate.
    Both my 3D Printers have home made filament run-out sensor's so there Actually a 3DP17's. Running Marlin 1.1.5 firmware.

  5. #5
    Super Moderator curious aardvark's Avatar
    Join Date
    Jul 2014
    Posts
    8,818
    what print surface did you use ?

  6. #6
    Staff Engineer Roberts_Clif's Avatar
    Join Date
    Jun 2017
    Location
    Washington State, USA
    Posts
    1,141
    Add Roberts_Clif on Thingiverse
    Replacement Hictop Surface with 3M 200MP adhesive.

  7. #7
    Congratulations!

    ABS has been a thorn in my side - I have never had a good structural print with it.

    I use PLA toughened with rubberizers (aka 'Tough', 'Raptor', or 'Advanced' PLA) for most everything these days.

  8. #8
    Staff Engineer Roberts_Clif's Avatar
    Join Date
    Jun 2017
    Location
    Washington State, USA
    Posts
    1,141
    Add Roberts_Clif on Thingiverse
    I would not say I have not printed good ABS prints. I am just over coming a few obstacles in my endeavour to learn the steps to a prefect 3D Print.

    This one is being able to keep my build surface from forming air bubbles at the ABS build surface temperatures.
    Most likely air was there the entire time and just expanded during the 1st few ABS builds, Air has been released now so may never occur again.

    ABS needed a Raft to print without warping
    Img_2100-1.jpg


    PLA was fine without a Raft.
    Img_2099-1.jpg
    Last edited by Roberts_Clif; 02-16-2019 at 12:55 PM.

  9. #9
    Hi Roberts,
    If you are still looking into printing ABS without warp, we still have few DustnPrint samples to give away for free on our main website.
    We have worked quite a bit on the website, and included videos, and links to our Instagram account.

    Best Regards,

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •