  1. Replies
    1
    Views
    150

    PETG is particular about starting height.. needs...

    PETG is particular about starting height.. needs to be correct. No idea how you configure that on your printer. I have use eSun PETG on clean glass at 80c Polyimide tape (sticks too well to that...
  2. 3d printed parts are most likely going to leak.....

    3d printed parts are most likely going to leak.. and pla would certainly not be the right choice for a part that could burst. Nylon/EPA, Taulman Alloy 910, maybe PETG, but no way would I attempt...
  3. Replies
    5
    Views
    488

    Keep in mind what the machine is actually doing.....

    Keep in mind what the machine is actually doing.. A solid plastic filament is being pushed into a tiny hot chamber to melt, then under pressure squeezed through a tiny hole which is suspended over a...
  4. Not something I really need.. If the print...

    Not something I really need.. If the print finishes.. the PS and and fan can run until I wake up...
  5. Replies
    5
    Views
    488

    if that is 80mmS then SLOW THE HECK DOWN! No...

    if that is 80mmS then SLOW THE HECK DOWN! No idea what you are printing but try the same model at 50mmS and see what changes.
  6. Thread: newby help

    by airscapes
    Replies
    4
    Views
    353

    De-lamination has always been printing too...

    De-lamination has always been printing too cold, at least for me. Try 225. Just because you have your hot end set to 225 does not mean it actually is.
    Sorry about the inaccurate size naming.....
  7. Thread: newby help

    by airscapes
    Replies
    4
    Views
    353

    Try slicing this 15x15x2x.6 mm square and...

    Try slicing this 15x15x2x.6 mm square and printing it. When complete measure it with your Digital caliper (you really need one if you want to do 3d printing) It should be 2mm tall within .02mm+-...
  8. Replies
    11
    Views
    3,348

    Google Denture repair epoxy

    Google Denture repair epoxy
  9. Replies
    21
    Views
    20,522

    You may want to look into Taulman 910, easy to...

    You may want to look into Taulman 910, easy to print and made for high strength part. Just started using it but liking it's ease of use and properties.
    Prints great in a .25 nozzle as as a .5.....
  10. Replies
    2
    Views
    375

    I have not used carbon fiber nylon but have just...

    I have not used carbon fiber nylon but have just started using Taulman 910 and had a print look like that when I printed too fast! Was shooting for 40mmS and entered 400mS :-) I don't use cura...
  11. Replies
    6
    Views
    1,354

    I really like heat set insert for putting part...

    I really like heat set insert for putting part together. You will need to design it for 3d printing and in pieces with the method of joinery you choose. Just like wood there are many methods to...
  12. Replies
    3
    Views
    514

    getting prints to stick to whatever the surface...

    getting prints to stick to whatever the surface has more to do with proper starting height than anything else. .03 to high and you are going to have problems.. add some tape and it takes up the...
  13. Replies
    6
    Views
    1,138

    Thanks, I will have to look into PET, did not...

    Thanks, I will have to look into PET, did not recall ever seeing that filament .. Does it go by other names, don't see it on the Esun list.. googling now..
  14. Replies
    6
    Views
    1,138

    PETG does not need an enclosure, it also does not...

    PETG does not need an enclosure, it also does not a fan.. Print it slow.. 40mmS or less..
  15. mine live on a dresser in a spare bedroom. ...

    mine live on a dresser in a spare bedroom. Besides the printer I have a Monitor, keyboard and mouse attached with a Raspberry pi using octoprint. The keyboard monitor and mouse are not required...
  16. Just got a roll of Taulman 910 which seems like...

    Just got a roll of Taulman 910 which seems like really neat stuff! I only printed a few cal squares and did not dry it first (was rather wet) but still printed very well with a .5 nozzle ate 250c...
  17. Replies
    3
    Views
    809

    PETG would be what I would use.

    PETG would be what I would use.
  18. I ordered 3 rolls of the Crystal PETG and it...

    I ordered 3 rolls of the Crystal PETG and it arrived as well as some of their PLA which was my first order. The PLA had a lot of variation in thickness and when I emailed them about it, the sent me...
  19. Yes the crystal PETG is in the picture. I also...

    Yes the crystal PETG is in the picture. I also have Red and Clear.. also about the same price when I bought it. On my M2 it prints at 245 with a bed temp of 80, I have been Elmers glue stick on the...
  20. it is not like TPU.. it is like hard plastic that...

    it is not like TPU.. it is like hard plastic that won't snap... when bent.. 123131231412315
  21. May want to try a TPU with a shore hardness of...

    May want to try a TPU with a shore hardness of 95. I have some stuff I got as a sample from someplace and it was way to hard for what I was doing (looking for a cheaper Nijaflex)As was said PETG is...
  22. Replies
    11
    Views
    2,416

    being able to design your own parts is very...

    being able to design your own parts is very helpful, however, you have a lot on your plate leaning how to produce a quality part from you 3D printer and slicer. I am focused on mechanical parts and...
  23. Replies
    5
    Views
    609

    I use jb weld plastic epoxy..

    I use jb weld plastic epoxy..
  24. Replies
    18
    Views
    1,631

    This is probably the best for the money at the...

    This is probably the best for the money at the moment...
  25. Thread: Show infill

    by airscapes
    Replies
    2
    Views
    408

    No idea in cura but if the is an option for...

    No idea in cura but if the is an option for number of top layers, set it to 0