My mistake, I must not have saved the profile as I usually run at 35% for most of my PLA parts.
I am currently test running PETG to see if I get better results. Any thoughts as to what would cause the material to goop up?
Printable View
I would try increasing your density, also check the "final printing temp" make it the same as the overall default temp